Abstract
The results of investigations of mechanical properties of the polyvinyl chloride foam and the epoxide composite reinforced by glass clothes and their fatigue life are presented. The fatigue life and the dependence of the structure degradation on the number of cycles of the sandwich plate subject to bending are also given. The plate was composed with the core made of the polyvinyl chloride foam and the face sheets of the epoxide composite reinforced by glass clothes.Keywords:
mechanical properties, fatigue investigations, fatigue life, structure degradation, sandwich plate, polyvinyl chloride foam, epoxide composite reinforced by glass clothes UKD symbolsReferences
1. R. GIELETA, A. KICZKO, S. OCHELSKI, The stand for fatigue tests of materials, Biuletyn WAT, no 7, 2000.
2. P. BRONSTED, S.J. ANDERSON, H. LILHOLT, Fatigue performance of glass/polyester laminates and the monitoring degradation, Ninth International Conference on the Mechanics of Composite Materials, Riga 1995.
3. F. SIDOROOFF, B. SUBAGIO, Fatigue damage modelling of composite materials from bending test, Sixth International Conference of Composite Materials, Vol. 4, London, New York 1987.
2. P. BRONSTED, S.J. ANDERSON, H. LILHOLT, Fatigue performance of glass/polyester laminates and the monitoring degradation, Ninth International Conference on the Mechanics of Composite Materials, Riga 1995.
3. F. SIDOROOFF, B. SUBAGIO, Fatigue damage modelling of composite materials from bending test, Sixth International Conference of Composite Materials, Vol. 4, London, New York 1987.